3D PRAI WHITE STONEWARE 5 KG VERPAKKING

The popular PRAI, high fire white body with 40% impalpable grog (up to 80 Mesh) adapted for 3D printing. Its particular white ivory colour after firing is much appreciated and provides an excellent ware for glazes and colouring oxides. Besides, its characteristics offer an excellent behaviour during drying and firing. Available in extruded body with the ideal humidity for 3D printing. Presented in a practical cylindrical format with double packaging. 

Firing range: 1240-1300ºC / Cone 6-10
Biscuit temperature: 1000ºC / Cone 06
Water content: 22%
Plasticity (IP Atterberg): 16
Carbonate content (CaCO3): 0%
Drying shrinkage: ˜8.5%
Firing shrinkage (1300ºC): 7.0%
Porosity (water absorption at 1300ºC): 0.0%
Dry bending strength: 3.0 N/mm2
Fired bending strength (1300ºC): 45.3 N/mm2
Thermal coefficient (25-500ºC): 52.6x10-7ºC-1